Suprême HT Amber Glass-Ceramic CAD Blocks

Suprême.cad is a kind of lithium disilicate glass- ceramic block which is suited for CAD/CAM applications.

Suprême.cad is packaged in sets of (5) in size 18-15-13 with Cerec mount.

Material Properties
Popular in chair-side system restorations for its outstanding aesthetics, dental lithium disilicate glass-ceramics (CAD/CAM) has lower hardness before crystallization and can be quickly milled to a crown. The final strength is greater than 300Mpa after crystallization.

This material can be utilized for high-efficiency aesthetic restorations such as: veneers, inlays, onlays, partial crowns, anterior crowns, posterior crowns etc.

This form of ceramic block is utilized in a CAD/CAM system in a crystalline state (with a lilac color appearance) which is manufactured on a CNC milling machine utilizing a grinding technique.

After milling is completed, a porcelain furnace is used to crystallize the material at a temperature of 840-850°C yielding a restoration with a bi-axial flexural strength of 420±60 MPa.

Suprême CAD blocks are available in (5) block colors: Amythest, white jade, pink, blue, an yellow amber and have been divided into one category according to translucency characteristics：

  • HT - High Translucency, VITA shades BL1 & BL2

DOWNLOAD THE USAGE INSTRUCTIONS
DOWNLOAD THE MATERIAL DATA SAFETY SHEET

Suprême CAD Amber is packaged in sets of (5) in size 18-15-13.

SKU: GCFB_AMBER
*
*
$57.00
Ship to
*
*
Shipping Method
Name
Estimated Delivery
Price
No shipping options
Material type should be selected according to the following criteria:
  • The color of the final restoration
  • The color of prepared abutment
  • The shape, size and thickness of the restoration
  • The processing technique of the restoration
  • The final restoration's bonding material and color of the adhesives
Indications:
Single-unit anterior prostheses, veneers, inlays, onlays, three-unit prostheses not involving molar restoration
  • Density (after crystallization) 2.46-2.52 g/cm3
  • Thermal Expansion Coefficient (after crystallization): 10.5*10 -6 /K (50-500°C)
  • Linear Shrinkage Rate: 0.10-0.26%
  • Vickers Hardness (after crystallization): 6500±200 MPa
  • Elastic Modulus (after crystallization): 50±10 GPa
  • Fracture Toughness (after crystallization): 2.8-3.8 MPa m-1/2
  • Chemical Solubility (after crystallization): < 100 μg/cm2
  • Three-Point Bend Flexural Strength (after crystallization) 420±60 MPa
 

Get the Material Safety Data Sheet